High mechanical properties and very good weldability due to a ingreased silicon content, suitable for operating temperatures up to 300°C.

Excelent corrosion resistance against oxidising air upto 950ºC. Good resistance against hot cracking due to the high Mo. content.

Solid drawn ,corrosion-resistant, chromium-nickel wire for welding heat-resistant austenitic steels of the 25% Cr, 20% Ni types. 310 has good general oxidation resistance, especially at high temperatures, due to its high Cr content. The alloy is fully austenitic and is therefore sensitive to hot cracking. The temperature limits for use under intermittent oxidation depend on cycle frequency. In no case shall a temperature of 1000°C be exceeded. This alloy can withstand relatively severe thermic shock, and is superior to type 309 L.

CEWELD 310LMo has been developed primarly to cope with the severe corrosion conditions existing in the urea industry. Therefore, this filler has excellent resistance to corrosion in ammonium carbamate and nitric acid

Scale resistance up to 1150ºC, crack and wear resistant, suitable for rebuilding wornout parts. Excelent corrosion resistance against high temperature liquid acids.

Stainless steel with excellent resistance to intercrystallin corrosion and wet corrosion up to 350°C (662 °F). Corrosion-resistance is similar to low-carbon CrNiMo steels/cast steel grades

CEWELD® SG CrMoV6  wire  is  used  for  welding  matching,  and  similar, composition  base  materials.  The  weld deposit provides  high  strength, actual strength being dependent on heat treatment  Preheat,  interpass  temperature and PWHT will  be dependent  on application and base material.

CEWELD® 316LSi Tig biedt een goede algemene corrosiebestendigheid, vooral tegen corrosie in zure en gechloreerde omgevingen. De legering heeft een laag koolstofgehalte waardoor het vooral wordt aanbevolen wanneer er een risico is op interkristallijne corrosie. Het hogere siliciumgehalte verbetert de laseigenschappen door het dun vloeibaar maken en resulteert in een gladde naad.

CEWELD® 316H Tig is designed for welding 316/316H austenitic stainless steels operating at high temperatures (500-800°C) under long term creep conditions. This filler metal can also be used for welding 321/321H and 347/347H grades in high temperature structural service. This is particularly important in thick highly restrained weldments, since the possibility of premature service failure by intergranular HAZ cracking is reduced by using more ductile weld metal rather than 347H.

Stainless steel with excelent resistance to intercrystalline corrosion and wet corrosion up to 350°C (662 °F). Corrosion-resistance is similar to low-carbon CrNiMo(Mn,N) steels/cast steel grades.Seawater resistant, good resistance to nitric acid, selective attack max. 200 μm.Non magnetic (permeability in field of 8000 A/m 1.01 max.).