410

Category 
GMAW-GTAW Solid wires
type 
Solid stainless steel welding wire
applications 
Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. 410 has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.
Properties 

410 is a martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition of 12% Chromium. These weld deposits are air-hardenable that can normally be heat-treated after welding.

classification
AWS 
A 5.9: ~ER 410
EN ISO 
14343-A: G Z 13
DIN: W.Nr. 
1.4009
DIN 
8556: SG-X 8 Cr 14
Suitable for 

For welding or repairing 12% Cr air-hardenable stainless steels like types 410, 416, 420, 431 and cast C-15, W.Nr: 1.4008, 1.4000, 1.4006, X8Cr14, X6Cr13, X10Cr13 and cast steels. 

welding positions: 
Weld deposit weight % (typical)

C

Mn

Si

Cr

Ni

Mo

0.10

0.52

0.7

13.0

0.25

-
mechanical properties

Heat

RP0,2

Rm

A5

Impact Energy (J) ISO-V

Hardness

Treatment

(N/mm2)

(N/mm2)

(%)

-20°C

-40°C

-60°C

HRc / HB

AW

35 HRc

PWHT 680C/8hr

>450

>650

>15

180 HB 30
PWHT: Post weld heat treatment
welding parameters packing

Welding Parameters

Packing

D (mm)

Voltage (V)

Current (A)

spool type

kg / 6pack

kg / pallet

1,0

K-300 / Drum

15 / 250

1080 / 1000

1,2

K-300 / Drum

15 / 250

1080 / 1000

1,6

K-300 / Drum

15 / 250

1080 / 1000
Tig welding
1000 mm cut lenghts are available on request from 1,2 till 3,2 mm in 5 kg tubes