Selectarc Fonte NiFe 2
CEWELD E FeNi 60 N is suitable for welding grey and malleable cast iron, equally suitable for SG iron. Use this type in case a high tensile strength is required or because of his non conductive coating to weld in difficult welding positions where coating contact is unavoidable with the base metal.
CEWELD E FeNi 60 N is suitable for welding grey and malleable cast iron, equally suitable for SG iron. Use this type in case a high tensile strength is required or because of his non conductive coating to weld in difficult welding positions where coating contact is unavoidable with the base metal.
CEWELD E FeNi 60 N has a few benefits compare to other “FeNi” types because of improvements, such as: weldable with very low current, non conductive coating and a powerful arc at very low amps. Preheating is normally done to slow down the cooling speed, in case you can not control the cooling speed it is better to keep the work peace at a low temperature during welding and hammer immediately after welding.
Spheroidal Cast Iron, Diluted Cast Iron, old Cast Iron, Steel to Cast Iron etc.
EN 1561: EN-GJL-100, EN-GJL-150, EN-GJL-200, EN-GJL-250, EN-GJL-300, EN-GJL-350, GG10, GG15; GG20, GG25; GG30; GG35; GG40
EN 1562: EN-GJMB-350, EN-GJMB-550 , EN- GJMW-350, EN- GJMW-550 , GTS 35, GTS 55, GTW 35, GTW 55
EN1563: EN-GJS-400-15, EN-GJS-400-18, EN-GJS-450-10, EN-GJS-500-7, EN-GJS-600-3, EN-GJS-700-2. GGG40, GGG45, GGG50, GGG60; GGG70, GGG80
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | >296 | 400 | >6 | 200 HB |
Build-up of cast iron and alloyed grey-cast iron Well suited for warm and in special applications for cold welding. Used to fill-in voids and pores, build-up of worn-down parts.
Build-up of cast iron and alloyed grey-cast iron Well suited for warm and in special applications for cold welding. Used to fill-in voids and pores, build-up of worn-down parts
Build-up of cast iron and alloyed grey-cast iron Well suited for warm and in special applications for cold welding. Used to fill-in voids and pores, build-up of worn-down parts.
Build-up of cast iron and alloyed grey-cast iron Well suited for warm and in special applications for cold welding. Used to fill-in voids and pores, build-up of worn-down parts
Very good welding and wetting characteristics and high resistance to cracks and fissures. Extreme good deposition rate compare to MMA.High strength and good bonding weld metal..
DIN GG15 – GG40, GGG40 - GGG70, GTS35 - GTS 65
ASTM: A48 Class 25 B - A48 Class 60 B, A536 Grad 60-80
FGL 150- FGL 400, FGS 400 12 - FGS 600 3, MN350 10 - MN650 3
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 200 HB |