MOST W 45
Solid wire
Rebuilding wornout parts that faces wear and impact combined with increased working temperatures.
Hot dies, dies, punches, hammer dies, drawing rings
Forging dies, mandrels slab shears, hot cuts, etc.
Rebuilding wornout parts that faces wear and impact combined with increased working temperatures.
Hot dies, dies, punches, hammer dies, drawing rings
Forging dies, mandrels slab shears, hot cuts, etc.
Machinable ,Heat resistant weld deposit with excelent wear resistance. The weld deposit can be heat treated to offer maximum service protection.
Tempered 560° C ~ 52 HRc
Tempered 450° C ~ 49 HRc
Tempered 350° C ~ 48 HRc
Soft annealed 250 HB
45-52 HRc
1.2567, 1.2365, 1.2713, 1.2714, 1.2581
30WCrV17 2, 32CrMoV12-283, 55NiCrMoV6, 55NiCrMoV7, X30WCrV9-3
Tempering : approx. 3 h / temperature depending on desired working hardness.
Soft annealing : 2 - 4 h at 800° C -840° C / furnace cooling
Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
---|---|---|---|---|
As Welded | 47 HRc | |||
580°C±15°C 1h | 53 HRc |