Thanks to its excellent weldability and good penetration this alloy is used mainly in construction and automotive industry. The silicon addition results in improved fluidity (wetting action), making the alloy the preferred choice of welders. The alloy is not sensitive to weld cracking and produces bright, almost smut-free welds. Not recommended for anodizing. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding.

The weld deposit is ductile and offers excellent corrosion resistance in oxidizing environments. The unique combination of mechanical strength and corrosion resistance makes the alloy a preferred choice in many applications to prefent or solve problems. The wire is cleaned in a very special way to obtain porosity free and a ductile weld deposit. 

• High quality alloyed copper wire • Sound, pore free deposits and good electrical conductivity • Excellent corrosion resistance

Very good deoxidization and high hardness similar to cast bronzes. Surfacing and joining of Copper and CuSn-Alloys. Widely used and recommended for oven soldering. High quality alloyed copper wire. Sound, pore free deposits and good electrical conductivity. Excellent corrosion resistance

The weld metal is a Cu-Al-Ni bronze. Sound, pore free deposits on ferrous and non-ferrous base materials. Seawater, wear and corrosion resistance; for example when seawater, cavitation and erosion are simultaneously affecting the weld deposit.

This Nickel weld deposit offers a easily machinable weld deposit with high ductility and no undercut.

Das Schweißgut des CEWELD 35-45Nb Tig ist in einer schwefelarmen, kohlenstoffanreichernden Atmosphäre bis zu 1175° C einsetzbar und hat eine ausgezeichnete Kriechfestigkeit und eine gute Beständigkeit gegen Aufkohlung und Oxidation.

Es ist keine Vorwärmung und Wärmenachbehandlung nötig.

Auf geringe Wärmeeinbringung achten und die Zwischenlagentemperatur sollte auf max. 150 °C begrenzt werden.

Melting Point 1112°F, Magnesium 92/8 is Mg - 9 Al - 2 Zn welding alloy which finds wide use for fabricating and repair welding of many similar compositions. Casting repair and refurbishment is the most common application.Magnesium 92/8 is preferred for joining many casting alloys.

This nickel based alloy offers superior wear protection, retaining its hardness up to 600ºC (1000ºF) with significant resistance to oxidation.

Excellent welding properties and mechanical strength up to 460 MPa yield strength. Excellent to be used for creep resisting service at temperatures up to 500 °C.