… abrasion resistance can be kept also with increased temperatures. For Hardfacing of more than 3 layers it is recommended to buffer with an … like CEWELD E DUR 350 Kb that delivers a welding deposit of less hardness. Overlays on steel with high tensile strength should be … resistant coating even in extreme humidity conditions! … Tubular Hardfacing alloy for Sugar Mill knives and Hammers, Clinker Crushers, …

… High C-Cr-Nb, B-alloyed flux-cored wire electrode which forms extremely hard complex carbides for extremely wear resistant deposits on parts … mixed gas. Extreme good wear resistance due to excelent first layer hardness properties. More than 1 or 2 layers should not be deposited. A … conveyor chains, agriculture, construction, mixer blades, paddles, cement pumps with excelent abrasion and wear resistance against sand …

… can be polished and is scale-resistant up to 900°C. The achievable hardness of the weld metal is mainly influenced by the dilution with … the dilution and the C content of the base material, the higher the hardness of the weld metal. The preheat and interpass temperature …

… Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/hour to 620ºC …

… Austenitic deposit with strain hardening properties and no limits in the number of layers. The deposit … The weld deposit offers fair corrosion resistance and has strain hardening properties. This alloy should be applied at highest impact … crushing hammers, dredger teeth, rollers, blast furnace, mantles, Hardfacing manganese hard stee, buffer layers etc.. … SACW MnCr … …

… very good corrosion resistance, shiny coating with a little higher hardness than SP 1.4115. The spray deposit cannot be machined with normal cutting tools, grinding is possible. Hardness approximately 50 HRc … Flame spray, electric spray and high …

… be maximum 250ºC. The weld metal is machinable with carbide tip tools, hardening is possible. The maximum hardness is dependent on the base metal and is usualy already achieved …

… deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degrees 20% at 600 °C and has a nominal hardness of 49-53 HRc at room temperature. The weld deposit is high … and abrasion resistance, Thermo shock resistant and impact resistant, Hardfacing valves, Seats, Pumps, Knives, Plastic recycling …

… metal to metal wear resistance combined with impact, despite the high hardness several layers can be applied without risk of chipping of. The weld deposit is temperature resistant up to 500°C and hardness will remain very well at increased temperatures. Scale …

… deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degreas 20% at 600°C and has a nominal hardness of 47-52 HRc at room temperature. The weld deposit is high … for hardfacing of engine valves, pinch rollers in the metal-processing industries, and rotor blade edges. … Powder PTA DUR 12 …