… impact and shock. The weld metal is machinable with carbide tip tools, hardening is possible. The maximum hardness is dependent on the base metal and is often achieved in the …

… abrasion resistance combined with heavy shocks, despite the high hardness several layers can be applied without any risk of braking out … sensitive base material preheating is recommended at 300 - 400 °C. Old Hardfacing layers should be removed, clean or grind properly before …

… deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degreas 20% at 600°C and has a nominal hardness of 49-53 HRc at room temperature. The weld deposit is high … and abrasion resistance, thermo shock resistant and impact resistant, hardfacing valves, seats, pumps, knives, plastic recycling …

… High C-, Cr- alloyed flux-cored wire electrode which forms extremely hard carbides for extremely hard deposits on parts subject to excessively heavy abrasive wear …

… alloy for the assembly and cladding of 17% chromium alloys and age Hardfacing components where heat and corrosion resistance similar to … deposit can withstand working temperatures up to 450°C and offers high hardness and wear resistance. … 1.4122 (G)X35CrMo17, Cast steels … MA …

… electro slag process. Due to the low dilution with the base metal a hardness exceeding 50 HRc can be achieved already in the first layer. Multiple layers can be applied to obtain full hardness at the final layer. Flux to be used FL 830 ESH … 52-58 HRc electro slag and / or submerged arc strip for hardfacing against schock and wear, Rebuilding wornout parts such as …

… weldability without slag losses. For critical base material or old hard facing layers it is necessary to buffer with an electrode like … E DUR 350 Kb / E 11018-G that delivers a welding deposit of less hardness. Overlays on steel with high carbon content should be buffered … 2 till 3 layers should be welded. … Sugar mill knives and Hammers, Cement mixers, Clinker crushers, Sintering lines, Fire gratings, Mixer …

… High C-, Cr- alloyed flux-cored wire electrode which forms extremely hard carbides for extremely hard deposits on parts subject to excessively heavy abrasive wear … metals.. Equivalent in SMAW: Dur 62S  … 60-64 HRc hardfacing alloy, Cement, Mineral mixing peddles, coke wear plates, Fan blades, screw …

… Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/ hour to …

… against sliding wear of metallic objects.It has a good retention of hardness up to 650°C and is non scaling up to 900° C thermo shock resistant and resistant to sudden changes of temperature.Work hardening. Not crack sensible.The number of layers can be done as …