SMAW Electrodes Enrobées

4830 Kb

High corrosion resistance and excellent weldability on both AC and DC+. The weld deposit is scale resistant up to 1000ºC

 

4455 Ti

Extreme stable arc on both AC and DC+ with no spatter losses. The slag is self lifting and leaves a fine rippled shiny surface.

AquaForce HR

AquaForce HR is a high recovery wet welding electrode that is double coated to offer maximum moisture and electrical resistance. AquaForce HR is able to produce beautiful flat filled welds with deep penetration without porosity. Filled welds exceeding an A height of 4,0 mm are easy to achieve in one single layer for high productivity. AquaForce HR can be used in all positions, especially suitable for vertical down (PG) position.

AquaForce LC

AquaForce LC est la première électrode de basique développée avec du "sable hydrophobe" pour offrir une résistance maximale à l'humidité. AquaForce LC est actuellement la seule électrode disponible qui peut produire des soudures plates (non concaves) avec une pénétration plus profonde dans toutes les positions, y compris PB, PC, PD, PE et PGL'analyse chimique spéciale du fil de l'âme  de cette électrode (très faible teneur en carbone et en manganèse) réduit la dureté du métal déposé et de la ligne de fusion, causée par la vitesse de refroidissement élevée (T8-5) du soudage sous-marin.

7018-1

L'électrode 7018-1 est une électrode à faible teneur en hydrogène adaptée aux joints fortement sollicités avec une soudabilité très facile et des propriétés mécaniques extrêmement élevées pour les aciers avec résistance à la traction jusqu'à 610 N/mm2 ainsi que pour les aciers à grain fin présentant une limite d'élasticité plus elevée. Il est particulièrement adapté au soudage sur AC et DC +. Le 7018-1 convient à l'acier contenant jusqu'à 0,6% de carbone et présente une

6013 T

6013 T is a thick coated electrode for joining and surfacing steel structures of all kinds in mechanical engineering, body and wagon building, in the fabrication of vessels and containers, and in shipbuilding. The 6013 T is eminently weldable and possesses excellent welding properties in all positions except vertically down. Easy strike, no spatter losses. Very easy slag removal. Smooth, finely rippled seam surface and low fume.

6013 S

6013S is a medium thick coated electrode for all kinds of steel structures and is particularly suited for welding jobs at poorly accessible points and badly prepared seams. The 6013S can be sued in all positions, in particular it is ideally suited for vertical down welds upto 3,2 mm. Viscous weld metal, hence good gap bridging. Easy slag removal and the electrodes can be bent very well to improve accessibility to hard to reach places.

9018-G

High basic offshore electrode according the latest offshore requirements for sub zero temperatures down to -60°C.  Suitable for steel types upto 550 N/mm2 yield strength, excellent welding properties and extreme low hydrogen content below 3 ml/100gr weld metal. The weldmetal is suitable for longer post weld heat treatments as applied in Riser applications.

9016-B9

9016-B9 is designed to weld equivalent ‘type T91’ T92 CrMo steels modified with small additions of Tungsten and Vanadium to give improved long term creep properties. These consumables are specifically intended for high integrity structural service at elevated temperature so the minor alloy additions responsible for its creep strength are kept above the minimum considered necessary to ensure satisfactory performance.

4501 Kb

Ceweld 4501 Kb is a basic coated electrode with a fully alloyed core, the duplex weld deposit provides exellent resistant to pitting, chloride stress corrosion cracking and intercrystalline corrosion due to the high CrMo(N) content (Pitting index >40). Furthermore, the weld metal alloy is saltwater-proof and offers high tensile strength, as a result of nitrogen being added to the alloy.
 