11018-H

type 
Ultra low hydrogen high basic offshore electrode for high strength fine grain steels.
applications 
Designed for welding steels with high yield strength >690N/mm2 in offshore, crane building, heavy transport, lifting etc.
Properties 

Mn, Ni, Cr and Mo alloyed basic electrode for welding low alloyed steels with yield strength >690 N/mm2. Crack resistant and well suited for low-temperatures, ductility down to -60°C. Preheating, interpass temperature and post weld treatment as required for the base metal. Hydrogen content: < 3 ml / 100 g weld metal. Ceweld 11018-H is packed in the best in class multi layer vacuum pack to avoid costly and time consuming redrying of the electrodes.

classification
AWS 
A 5.5: E 11018-M-H4
EN ISO 
18275-A: E 69 6 Mn2NiCrMo B 42 H5
DIN 
8529: EY 69 77 Mn2NiMo B H5
Suitable for 

Weldox 700, naxtra 70, S690, dilimax, S690QL1, S620, S550, Hardox, S620Ql1, S690QL1, S600MC, S700MC, Naxtra 63, Naxtra 70, Optim 700 mc plus, TStE620, TStE690, Weldox 500, Hardox, Domex 460 MC, Domex 500 MC, Domex 550 MC, Domex 600 MC, Domex 650 MC, Domex 700 MC,  L480 - L550, X65 - X80, Hardox 400, XAR 400, Dilidur 400, 20MnCr65, 28CrMn43.

approvals 
DNV 5Y69, Lloyds 5Y69, CR, CE approved
welding positions: 
weld deposit weight %

C

Mn

Si

Cr

Ni

P

S

Mo

V

0,045-0,075

1,40-1,60

0,30-0,45

0,30-0,40

1,90-2,20

<0.025

<0.025

0,30-0,40

<0,25

mechanical properties

Heat

RP0,2

Rm

A5

Impact energy (J) ISO-V

Hardness

treatment

(N/mm2)

(N/mm2)

(%)

-20°C

-40°C

-60°C

HRc / HV

AW

>690

>770

>17

>110

>80

>69

SR

>690

>770

>19

>32

AW: as welded / SR: stress releived (PWHT) 580°C/2hr
redrying temperature 
400°C/1 hr
welding parameters / packing

Welding Parameters

Packing

D (mm)

Length (mm)

Current (A)

kg / vacuum pack

pcs / vacuum pack

kg / master carton

2,5

350

70-90

0,8

33

8,0

3,2

350

90-125

0,7

18

7,0

4,0

350

120-160

0,8

14

8,0

Disclaimer: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained, the information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and any liability incurred from any reliance thereon is expressively disclaimed. Typical data are those obtained when welded and tested in accordance to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Other tests and procedures may produce different results. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application. The selection and use of specific products is solely within the control of, and remains the sole responsibility of the customer. The right to change design and/or specifications without notice is reserved.