… against hot cracking due to the high Mo content. During build-up welding, the weld metal already achieves approximately the composition …

… Use a larger tip than is generally recommended for same diameter mild steel. Use slight excess acetylene feather. The deposit is not … rod or endless on coils. … Dur R (Ni) can be applied on all sorts of steels except on cast iron or Mn-steel. The main applications are hardfacing and rebuilding of …

… 3 (according to Boniszewski) Current: DC or AC, in single or multi-wires Grain size: 2-20 … S355, S420, S460, X65, X70, X80 … FL 160 … …

… wire, guarantees optimum metallurgical  quality, economic positional welding and attractive welder appeal.Very good resistance against …

… requirements at sub zero temperatures down to -60 °C. Excellent welding properties. Yield strength > 550 MPa. Low hydrogen content HD < …

… solid wire for the GMAW/GTAW of low-temperature, fine-grained steels suitable for NACE requirements. The deposit provides good impact …

… a slightly higher percentage of phosphor, suitable for MIG welding, easy to handle, high plasticity of the weld metal. High …

… range of alloys. Thicker sections should be preheated (150°C) prior to welding. … Aluminium alloys: AlMg4,5Mn, AlMg5, AlMg2Mn0,8, AlZnMg1, …

… Ductile welding deposit with high conductivity and corrosion resistance. The … than 5 mm should be preheated up to approximately 500 °C. … Cladding steel, Grey cast iron, Copper, Copper Alloys and dissimilar welding.  Mat.n: 2.0040, 2.0060, 2.0070, 2.0076, 2.0080, 2.0090, 20100, …

… on wire diameter) tungsten carbides. OA WC2-Fe  has good welding characteristics. Multi-layer deposits are not recommended due …